ATTANE™ 4607GC

About
ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer is a skin layer in cast film offers excellent low temperature hot tack properties combined with outstanding tear and impact strength. In stretch film applications, ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer exhibits excellent stretchability as well as good physical and cling properties. ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer can also be utilised in blown film coextrusion where it is combined with other resins having excellent bubble stability allowing ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer to be used as a sealant in multilayer film structures. Applications: Cling layer in cast stretch film. Sealants in cast and blown films. Complies with: EU, No 10/2011- U.S. FDA FCN 741 Consult the regulations for complete details&&

About

ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer is a skin layer in cast film offers excellent low temperature hot tack properties combined with outstanding tear and impact strength. In stretch film applications, ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer exhibits excellent stretchability as well as good physical and cling properties. ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer can also be utilised in blown film coextrusion where it is combined with other resins having excellent bubble stability allowing ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer to be used as a sealant in multilayer film structures. Applications: Cling layer in cast stretch film. Sealants in cast and blown films. Complies with: EU, No 10/2011- U.S. FDA FCN 741 Consult the regulations for complete details&&

Product Description
Supplier	DOW
Generic	VLDPE
Material Status	Commercial: Negative
Availabilitys	Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.904	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	4.0	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	23	µm
Membrane puncture strength
23 µm	5.00	J	Internal Method
Membrane puncture force
23 µm	48.0	N	Internal Method
tensile strength			ISO 527-3
MD, yield, 23 µ m	4.30	MPa	ISO 527-3
TD, yield, 23 µ m	3.60	MPa	ISO 527-3
MD, fracture, 23 µ m	33.0	MPa	ISO 527-3
TD, fracture, 23 µ m	23.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 23 µ m	500	%	ISO 527-3
TD, fracture, 23 µ m	630	%	ISO 527-3
Drop hammer impact
23 µm	180	g	ISO 7765-1/A
Elmandorf tear strength			ASTM D1922
MD：23 µm	190	g	ASTM D1922
TD：23 µm	390	g	ASTM D1922
Unstretched bonding	130	g	ASTM D4649

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	72.0	℃	ASTM D1525

optical performance	Nominal value	Unit	Test method
gloss
45°，23 µm	92		ASTM D2457
Haze
23 µm	0.70	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	190 to 260	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.