| About |
|---|
| This is a recycled PCABS from post-consumer sources and modified for technical applications demanding improved properties: Increased heat deflection temperature Improved cold impact behavior Improved non-flammability Increased notched impact strength&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Flame Characteristics,High Heat Resistance,low-temperature impact resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | Internal Method |
| Melt Flow Rate | |||
| 240℃，5.0kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| — | 0.53 | % | ISO 294-4 |
| 48 hrs | 0.58 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| 23℃ | 50.0 | MPa | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30℃ | 10 | kJ/m² | ISO 179/A |
| 23℃ | 25 | kJ/m² | ISO 179/A |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 90 | kJ/m² | ISO 179 |
| 23℃ | 140 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 25 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 100 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 115 | ℃ | ISO 306/A50 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 235 to 260 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Melt temperature | 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |