| About |
|---|
| Duratron® T7130 is a Polyamide-imide (PAI) product filled with carbon fiber. It can be processed by extrusion and is available in Latin America or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | PAI |
| Material Status | Commercial: Active |
| Features | Ethanol tolerance,Acidproof,Solvent resistance,Hydrocarbons,Resistance to salt water/fog |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.0 to 0.15 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.26 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 22300 | MPa | ASTM D1708 |
| — | 16500 | MPa | ASTM D638 |
| tensile strength | 221 | MPa | ASTM D638 |
| tensile strength | 203 | MPa | ASTM D1708 |
| Tensile strain | |||
| fracture | 6.0 | % | ASTM D1708 |
| fracture | 1.5 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 23℃ | 19900 | MPa | |
| 232℃ | 15700 | MPa | |
| bending strength | ASTM D790 | ||
| 23℃ | 350 | MPa | |
| 232℃ | 174 | MPa | |
| Compression modulus | 9860 | MPa | ASTM D695 |
| compressive strength | 254 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 48 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 320 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 282 | ℃ | ASTM D648 |
| Thermal conductivity coefficient | 0.52 | W/m/K | ASTM C177 |
| Linear coefficient of thermal expansion | 9.0E-6 | cm/cm/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 177 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 304 | °C | |
| Nozzle temperature | 371 | °C | |
| Mold temperature | 199 to 216 | °C | |
| Back pressure | 6.89 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Screw length to diameter ratio | 18.0:1.0 to 24.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1-10, 1=Easier to Machine |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |