| 30% Glass Reinforced, Heat Stabilized, Flame Retardant (halogen- phosphorous-free)&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low to no phosphorus content,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | |
| Shrinkage rate | |||
| TD | 0.90 | % | |
| MD | 0.55 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.6 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.5 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7000 | MPa | |
| tensile strength | |||
| fracture | 82.0 | MPa | |
| Tensile strain | |||
| fracture | 2.5 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 32 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 180 | ℃ | |
| Melting temperature | 220 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 425 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.8 mm | V-2 | ||
| 1.6 mm | V-2 | ||
| Glowing wire flammability index | |||
| 0.75 mm | 960 | ℃ | |
| 1.6 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 0.75 mm | 700 | ℃ | |
| 1.6 mm | 725 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 225 to 235 | °C | |
| Barrel middle temperature | 230 to 240 | °C | |
| Barrel front temperature | 235 to 250 | °C | |
| Nozzle temperature | 235 to 255 | °C | |
| Processing (melt) temperature | 235 to 260 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |