Orevac® OE825

About
Linear low-density polyethylene tie resin for coextrusion OREVAC® OE825 is a maleic anhydride modified linear low-density polyethylene adhesive resin. It is available in pellet form for use in conventional extrusion and coextrusion equipments designed to process polyethylene (PE) resins. Applications OREVAC® OE825 has been designed to develop a reliable bonding strength in coextrusion processes between polyethylene or ethylene copolymers and different materials among which polyamides and EVOH. Containing a higher amount of grafted reactive functionalities compared to standard LLDPE based coextrusion tie resins. OREVAC® OE825 can be used pure or blended with other polyolefins. It can be processed within different coextrusion technologies including cast film, blown film, sheet calandering, blow molding or tube extrusion.&&

About

Linear low-density polyethylene tie resin for coextrusion OREVAC® OE825 is a maleic anhydride modified linear low-density polyethylene adhesive resin. It is available in pellet form for use in conventional extrusion and coextrusion equipments designed to process polyethylene (PE) resins. Applications OREVAC® OE825 has been designed to develop a reliable bonding strength in coextrusion processes between polyethylene or ethylene copolymers and different materials among which polyamides and EVOH. Containing a higher amount of grafted reactive functionalities compared to standard LLDPE based coextrusion tie resins. OREVAC® OE825 can be used pure or blended with other polyolefins. It can be processed within different coextrusion technologies including cast film, blown film, sheet calandering, blow molding or tube extrusion.&&

Product Description
Supplier	Arkema
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Good bond,Low density,Agglomerability
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.913	g/cm³	ASTM D1505
Density	0.913	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.0	g/10min	ISO 1133
190℃，2.16kg	3.0	g/10min	ASTM D1238

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	99.0	℃	ASTM D1525 3
Vicat Softening Temp	99.0	℃	ISO 306/A
Melting temperature	118	℃	ISO 11357-3

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	160 to 180	°C
Barrel 2 zone temperature	180 to 200	°C
Barrel 3 zone temperature	200 to 220	°C
Barrel 4 zone temperature	210 to 230	°C
Barrel 5 zone temperature	220 to 230	°C
Connector temperature	220 to 230	°C
Nozzle temperature	220 to 240	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.