| Moplen RP348R is a polypropylene random copolymer with good flowability which is used in injection molding applications. Moplen RP348R is nucleated, for improved productivity and very good optical properties (transparency and brilliance). Its antistatic additivation prevents dust deposits and eases items demolding. Typical applications of Moplen RP348R are caps & closures, housewares and rigid packaging items.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good liquidity,Nucleation,Random copolymer,Antistatic property |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 25 | g/10min | ASTM D1238 | |
| 230℃，2.16kg | 25 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 45 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 85.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 76.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 130 | ℃ | ISO 306/A50 |
| B50 | 72.0 | ℃ | ISO 306 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 85 | ASTM D2457 | |
| Haze | |||
| 1000 µm | 9.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 60.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1150 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 29.0 | MPa | ASTM D638 |
| yield | 30.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 13 | % | ASTM D638 |
| yield | 14 | % | ISO 527-2 |
| fracture | > 50 | % | ISO 527-2 |
| Bending modulus | 1050 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |