| About |
|---|
| Diofan® A 602 is a water based dispersion of a polyvinylidene chloride copolymer. It is free of solvent traces, alkylphenol ethoxylates or any other toxic substances. It features strong barrier properties to water vapor and very low water absorption. Diofan® A 602 also offers very good resistance to oil and benzene. Due to a very low MFFT, this waterborne binder can be applied at low temperature as a flexible and tack free film. Diofan® A 602, as chlorinated based latex, combines also fire retardant properties. End uses are for example: Barrier and sealing coatings Flame resistant coatings Fiber and textile coatings Substrates can be concrete, cement, wood, gypsum, paper, fiberboard, fabrics and others.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDC |
| Material Status | Commercial: Active |
| Features | Low or no water absorption,Low odor,Flame Characteristics,Moisture resistance,Grease resistance,Nontoxicity |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| PH value | 4.0 | ||
| surface tension | 33 | mN/m | |
| Film-forming property | |||
| Minimum film-forming temperature | 5 | ℃ | |
| Solid content | 55 | % | |
| Density | |||
| Disperse (wet) | 1.260 | g/cm³ | |
| Coating (dry) | 1.580 | g/cm³ | |
| Lotion type | 阴离子 | ||
| Viscosity shear gradient 250 seconds ^ -1 | |||
| 23℃ | 19 | mPa·s | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Water vapor transmittance | |||
| 38℃，90% RH，1.0 µm | 160 | g/m²/24 hr | ASTM F1249 |
| Oxygen transfer rate | |||
| 25℃，0% RH，1 µm | > 1000 | cm³/m²/bar/24 hr | ASTM D3985 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 7.00 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Shelf life | 12 | month |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Glass transition temperature TG measured with a dried Diofan® A 602. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |