| About |
|---|
| LNP STAT-KON FX98500C is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Conductive |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.976 | g/cm³ | ASTM D792 |
| Density | 0.976 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 1.9 to 2.2 | % | ASTM D955 |
| MD：24 hrs | 2.7 to 3.0 | % | ASTM D955 |
| TD：24 hrs | 1.9 to 2.2 | % | ISO 294-4 |
| MD：24 hrs | 2.7 to 3.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.020 | % | ISO 62 |
| 24hr，50% RH | 0.020 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1080 | MPa | ASTM D638 |
| Tensile modulus | 871 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 14.0 | MPa | ISO 527-2 |
| fracture | 13.9 | MPa | ASTM D638 |
| yield | 23.9 | MPa | ASTM D638 |
| yield | 23.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 43 | % | ASTM D638 |
| fracture | 83 | % | ISO 527-2 |
| yield | 14 | % | ISO 527-2 |
| yield | 16 | % | ASTM D638 |
| Bending modulus | 870 | MPa | ASTM D790 |
| Bending modulus | 931 | MPa | ISO 178 |
| bending strength | 26.5 | MPa | ASTM D790 |
| bending strength | 27.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 48 | J/m | ASTM D256 |
| 23℃ | 5.8 | kJ/m² | ISO 180-1A |
| 23℃ | No Break | ASTM D4812 | |
| Notched impact strength of cantilever beam | |||
| 23℃ | No Break | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 21.4 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 63.2 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 48.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 46.7 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+2 to 1.0E+5 | ohms·cm | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 193 to 204 | °C | |
| Barrel middle temperature | 210 to 221 | °C | |
| Barrel front temperature | 221 to 232 | °C | |
| Processing (melt) temperature | 232 | °C | |
| Mold temperature | 38 to 54 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |