| Kingfa HC-110是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa HC-110的主要特性为:阻燃/额定火焰。 Kingfa HC-110的典型应用领域为:汽车行业&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Electroplating,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 200℃，5.0kg | 1.8 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 20 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃，3.2mm | 330 | J/m | ASTM D256 |
| 23℃，6.4mm | 300 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 96.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 87.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 103 | ℃ | ASTM D1525 3 |
| — | 95.0 | ℃ | ASTM D1525 4 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 23 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| tensile strength | 44.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 25 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ASTM D790 |
| bending strength | 66.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 182 to 205 | °C | |
| Barrel middle temperature | 205 to 230 | °C | |
| Barrel front temperature | 215 to 240 | °C | |
| Processing (melt) temperature | 220 to 245 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 0.00 to 0.0100 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |