| CALIBRE™ 300-10 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, and optical clarity. The CALIBRE 300-10 series products are available in 4 additive packages: CALIBRE 300: No mold release or UV Stabilizer. CALIBRE 301: Mold release. CALIBRE 302: UV stabilizer. CALIBRE 303: Mold release and UV stabilizer Govt. and Industry Standards: CSA (Canadian Standards Association) Underwriters Laboratory, Inc. (UL) Applications: Appliances Storage media housings Business equipment Electrical components Lighting Transportation Houseware Recreation Packaging applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,HB |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.20 | g/cm³ | ASTM D792，ISO 1183-A |
| — | 1.2 | g/cm³ | ISO 1183-3 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238，ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| Water absorption rate | ASTM D570 , ISO 62 | ||
| 23℃，24hr | 0.15 | % | ASTM D570，ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ASTM D570，ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eA |
| -30℃ | 13.0 | kJ/m² | ISO 179/1eA 3 |
| 23℃ | 90.0 | kJ/m² | ISO 179/1eA 3 |
| Charpy impact strength | ISO 179/1eU 3 | ||
| -30℃ | 无断裂 | ISO 179/1eU 3 | |
| 23℃ | 无断裂 | ISO 179/1eU 3 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 910 | J/m | ASTM D256 |
| 23℃ | 90 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ASTM D256 , ISO 180 | |
| Dart impact equipped with measuring instruments | |||
| 23 ℃, total energy | 87.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 144 | ℃ | ASTM D648，ISO 75-2/B |
| 0.45 MPa | 145 | ℃ | ISO 75-2 3 |
| 1.8 MPa, unannealed | 128 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 141 | ℃ | ASTM D648，ISO 75-2/A |
| 1.8 MPa | 131 | ℃ | ISO 75-2 3 |
| Vicat Softening Temp | |||
| B50 | 149 | ℃ | ASTM D1525 8 , ISO 306/B50 8 |
| B50 | 149 | ℃ | ISO 306 3 |
| Ball pressure temperature | 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD | |||
| -40 to 82 ℃ | 6.8E-5 | cm/cm/℃ | ASTM D696 |
| — | 7.0E-5 | cm/cm/℃ | ISO 11359-2 3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| — | 2.0E+17 | ohms·cm | ASTM D257 |
| — | > 1.0E+15 | ohms·cm | IEC 60093 3 |
| Dielectric strength | 17 | kV/mm | ASTM D149，IEC 60243-1 |
| Dielectric constant | |||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 , IEC 60250 3 | |
| 100 Hz | 3.00 | IEC 60250 3 | |
| Dissipation factor | |||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150 , IEC 60250 3 | |
| 100 Hz | 1.0E-3 | IEC 60250 3 | |
| Compared to the leakage tracing index | |||
| 2.00 mm, solution A | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Flame retardant level | |||
| 3.20 mm | HB | ISO 1210 3 | |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| Average combustion degree | 3 | cm | ASTM D635 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 , ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 73 | ASTM D785 | |
| R-level | 118 | ASTM D785 | |
| Tensile modulus | |||
| — | 2410 | MPa | ASTM D638 |
| — | 2300 | MPa | ISO 527-2/50 , ISO 527-2 3 |
| tensile strength | |||
| yield | 60.0 | MPa | ASTM D638 |
| yield | 60.0 | MPa | ISO 527-2/50 , ISO 527-2 3 |
| fracture | 71.0 | MPa | ASTM D638 |
| fracture | 71.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 , ISO 527-2 3 |
| fracture | 150 | % | ASTM D638 |
| fracture | 150 | % | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 3 |
| Bending modulus | |||
| — | 2410 | MPa | ASTM D790 |
| — | 2400 | MPa | ISO 178 |
| bending strength | |||
| — | 96.5 | MPa | ASTM D790 |
| — | 97.0 | MPa | ISO 178 |
| Wear resistance | 45 | % | ASTM D1044 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 2.0 in/min |
| 4. Method I (3 point load), 0.079 in/min |
| 5. 0.079 in/min |
| 6. 11.1 ft/sec |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 8. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |