| Compound based on PA6 first choice natural colour. With glass fibres 25%.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 to 1.33 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7500 to 8000 | MPa | ISO 527-2/1A/1 |
| tensile strength | ISO 527-2/1A/5 | ||
| yield | 125 to 135 | MPa | ISO 527-2/1A/5 |
| fracture | 125 to 135 | MPa | ISO 527-2/1A/5 |
| Tensile strain | ISO 527-2/1A/5 | ||
| yield | 2.0 to 3.0 | % | ISO 527-2/1A/5 |
| fracture | 2.0 to 3.0 | % | ISO 527-2/1A/5 |
| Bending modulus | 7000 to 7500 | MPa | ISO 178 |
| bending strength | 165 to 175 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 to 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 50 to 60 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 80 to 90 | J/m | ASTM D256-A |
| 23℃ | 60 to 70 | kJ/m² | ASTM D256 |
| 23℃ | 8.0 to 9.0 | kJ/m² | ASTM D256 |
| 23℃ | 7.0 to 8.0 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 50 to 60 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 210 to 220 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 215 to 225 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.2 mm | 200 to 210 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 210 to 220 | ℃ | ISO 306/A120 |
| B120 | 205 to 215 | ℃ | ISO 306/B120 |
| Melting temperature | 210 to 225 | ℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Notch E |
| 4. Notch A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |