| PA 3200 GF is a whitish, glass-filled polyamide 12 powder, which is characterised by an excellent stiffness in combination with good elongation at break. Laser-sintered parts made from PA 3200 GF possess excellent material properties: high stiffness high mechanical wear-resistance good thermal loadability excellent surface quality high dimensional accuracy and detail resolution good processability excellent long-term constant behaviour A typical application for PA 3200 GF is the usage e.g. for final parts within the engine area of cars, for deep-drawing dies or any other application which requires particular stiffness, high heat distortion temperature and low abrasive wear.&& |
| Product Description | |
|---|---|
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,Low coefficient of friction,High Heat Resistance,Good Tensile Strength,Good wear resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | 3D Printing, Laser Sintering/Melting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.2 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 21 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 157 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 96.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 179 | ℃ | ISO 306/A50 |
| B50 | 166 | ℃ | ISO 306 |
| Melting temperature | 176 | ℃ | ISO 11357 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 80 | ISO 868 | |
| Ball hardness | 98.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 3200 | MPa | ISO 527-2 |
| — | 2500 | MPa | ISO 527-2 |
| tensile strength | |||
| — | 51.0 | MPa | ISO 527-2 |
| — | 47.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 9.0 | % | ISO 527-2 |
| fracture | 5.5 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2900 | MPa | ISO 178 |
| bending strength | 73.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Z Direction |
| 3. X Direction |
| 4. Y Direction |
| 5. 20°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |