Daplen™ EF150HP

About
Daplen EF150HP is a mineral filled elastomer modified high performance polypropylene compound intended for injection moulding. This material has excellent balanced mechanical properties, gives a good surface quality and is easy to process. Applications Daplen EF150HP has been developed especially for the automotive industry. Body panels Bumpers Exterior trims Rocker panels Front grills Special Features Available with and without UV-stabilisation Low thermal expansion Excellent stiffness at low density High surface aesthetics&&

About

Daplen EF150HP is a mineral filled elastomer modified high performance polypropylene compound intended for injection moulding. This material has excellent balanced mechanical properties, gives a good surface quality and is easy to process. Applications Daplen EF150HP has been developed especially for the automotive industry. Body panels Bumpers Exterior trims Rocker panels Front grills Special Features Available with and without UV-stabilisation Low thermal expansion Excellent stiffness at low density High surface aesthetics&&

Product Description
Supplier	Borealis AG
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Good surface appearance,Renewable resources,Heat Stabilized
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.01	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	22	g/10min	ISO 1133
Shrinkage rate	0.70	%	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Bending modulus	2100	MPa	ISO 178
bending strength	29.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-20℃	4.5	kJ/m²	ISO 179/1eA
23℃	29	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-20℃	75	kJ/m²	ISO 179/1eU
23℃	No Break		ISO 179/1eU
Impact strength of cantilever beam notch			ISO 180/1A
-20℃	4.3	kJ/m²	ISO 180-1A
23℃	25	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	57.0	℃	ISO 75-2/Ae
0.45 MPa, unannealed	110	℃	ISO 75-2/Be
Vicat Softening Temp
—	136	℃	ISO 306/A
—	50.0	℃	ISO 306/B
Linear coefficient of thermal expansion
MD	5.4E-5	1/℃	Internal Method

Process Conditions
injection	Nominal value	Unit	Test method
Mold temperature	30 to 50	°C
Hold pressure	30.0 to 60.0	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.