| About |
|---|
| Celazole TF-60C is a carbon-reinforced blend, ideal for parts that require high strength, very low creep, and deflection resistance. A great match for planetary gears, office equipment, semiconductor, electronic and mechanical applications.&& |
| Product Description | |
|---|---|
| Generic | PBI |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Good wear resistance,Solvent resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.15 | % | ASTM D570 |
| balance | 4.0 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 320 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：24~149℃ | 2.6E-5 | 1/℃ | TMA |
| Thermal conductivity coefficient | |||
| 24℃ | 0.45 | W/m/K | ASTM F433 |
| Heat Capacity（70℃） | 1170 | J/kg/℃ | DSC |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Initial weight loss temperature | Internal Method | ||
| Air | 599 | ℃ | Internal Method |
| nitrogen | 627 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| A-level | 30 | ASTM D785 | |
| Tensile modulus | 24100 | MPa | ASTM D638 |
| tensile strength | 228 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.4 | % | ASTM D638 |
| Bending modulus | 21000 | MPa | ASTM D790 |
| bending strength | 321 | MPa | ASTM D790 |
| Compression modulus | 3790 | MPa | ASTM D695 |
| compressive strength | 221 | MPa | ASTM D695 |
| Poisson’s ratio | 0.39 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |