| About |
|---|
| Cheng Yu C1100 is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific. Characteristics include: Flame Rated High Flow Impact Resistant&& |
| Product Description | |
|---|---|
| Supplier | Cheng Yu |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.50 | % | ISO 294-4 |
| TD | 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| (23°C, 饱和) | 0.60 | % | ISO 62 |
| Melt Flow Rate | 20 | g/10min | ASTM D1238 |
| Water absorption rate | 0.20 | % | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 100 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B120 | 123 | ℃ | ISO 306/B120 |
| B50 | 120 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.200 | W/m/K | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | ≥1.0E+15 | Ω.cm | IEC 60093 |
| Surface resistance | ≥1.0E+15 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 0.800mm, in oil | 35.0 | KV/mm | IEC 60243-1 |
| 1.60mm in oil | 25.0 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.7 | IEC 60250 | |
| 50-60 Hz | 2.8 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.0070 | IEC 60250 | |
| 50-60 Hz | 0.0020 | IEC 60250 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| Insulation strength | 17.0 | KV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Relative temperature of heating wire | |||
| 1.00mm | 650 | ℃ | IEC 60695-2-13 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 117 | ISO 2039-2 | |
| tensile strength | |||
| 屈服，50mm/min，23°C | 55.0 | MPa | ISO 527-2 |
| 23℃，50 mm/min | 45.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃, 50 mm/min | 4.0 | % | ISO 527-2 |
| 50 mm/min，23℃ | ≥50 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃，1 mm/min | 2400 | MPa | ISO 527-2 |
| bending strength | |||
| Yield, 2 mm/min, 23 ℃ | 80.0 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/min，23℃ | 2300 | MPa | ISO 178 |
| Taber abrasion test | 79 | mg/1000 Cycles |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 41.0 | kJ/m² | ISO 180-1A |
| -30℃ | 17.0 | kJ/m² | ISO 180-1A |
| Charpy Notched Impact Strength | |||
| 23℃ | 42.0 | kJ/m² | ISO 179/1eA |
| -30℃ | 20.0 | kJ/m² | ISO 179/1eA |
| Notched impact strength of cantilever beam | NB | ISO 180/1U |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |