| Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms. Typical applications Cable jackets, plugs and terminations, spiral tubing, Films, ski-boot shells, ear tags, technical mouldings like mining screens, railway pads, seals.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Antimicrobial properties,Low temperature toughness |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 73 | ASTM D2240 | |
| Tensile modulus | |||
| injection molding | 524 | MPa | ASTM D412 |
| Bending modulus | |||
| injection molding | 503 | MPa | ASTM D790 |
| Taber abraser | 75.0 | mg | ASTM D1044 |
| Abrasion（DIN） | 35 | mm³ | DIN 53516 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 49.0 | MPa | ASTM D412 |
| 300% strain | 49.0 | MPa | ASTM D412 |
| 100% strain | 38.6 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D412 |
| tear strength | 280 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 40 | % | ASTM D395B |
| 70℃，22 hr | 60 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 33.0 | ℃ | Internal Method |
| Vicat Softening Temp | 160 | ℃ | ASTM D1525 |
| Softening temperature | |||
| DMA | 148 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.030 | % | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 210 to 230 | °C | |
| Barrel front temperature | 210 to 230 | °C | |
| Nozzle temperature | 220 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. after storage in water at 80°C for 42 days |
| 3. Method Bb, Angle (Nicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |