| About |
|---|
| LNP LUBRICOMP LFL36E is a compound based on Polyetheretherketone containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Wear Resistant, Easy Molding. Also known as: LNP* LUBRICOMP* Compound LFL-4036 EM Product reorder name: LFL36E&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Lubricating,Good wear resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.64 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 177 | MPa | ISO 527-2/5 |
| fracture | 170 | MPa | ASTM D638 |
| yield | 176 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| fracture | 2.0 | % | ISO 527-2/5 |
| yield | 2.0 | % | ASTM D638 |
| Bending modulus | 11400 | MPa | ISO 178 |
| 50 mm span | 11700 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 263 | MPa | ASTM D790 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.49 | ASTM D3702 Modified | |
| static state | 0.73 | ASTM D3702 Modified | |
| Wear factor | ASTM D3702 Modified | ||
| Ring | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Washer | 64.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 100 | J/m | ASTM D256 |
| 23℃ | 860 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 13.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 322 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 327 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 337 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 339 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 3.6E-5 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 1.8E-5 | 1/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 349 to 360 | °C | |
| Barrel middle temperature | 366 to 377 | °C | |
| Barrel front temperature | 382 to 393 | °C | |
| Processing (melt) temperature | 382 to 388 | °C | |
| Mold temperature | 138 to 166 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |