| Rubber modified (PC+SAN) blend; 10% glass fibre reinforced; Vicat/B 120 temperature = 130 °C; very good flow; improved impact strength; improved elongation at break; for demanding applications in the automotive interior |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+AS(SAN) |
| Material Status | Commercial: Active |
| Features | Good liquidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 4300 | MPa | ISO 527-1-2 |
| Tensile stress | |||
| Yield, 23 ° C | 60.0 | MPa | |
| Fracture, 23 ° C | 42.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ° C | 4.2 | % | |
| Fracture, 23 ℃ | 10 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 14 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 45 | kJ/m² | |
| 23℃ | 60 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 130 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 114 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 128 | ℃ | ISO 306 |
| — | 130 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 4.3E-5 | 1/℃ | |
| TD：23~55°C | 7.5E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 23 ℃，1 mm | 36 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 23℃，100 Hz | 3.30 | ||
| 23℃，1 MHz | 3.20 | ||
| Dissipation factor | |||
| 23℃，100 Hz | 3.1E-3 | ||
| 23℃，1 MHz | 0.013 | ||
| Compared to the leakage tracing index | |||
| Solution A | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.9 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| 23℃ | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 16.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：260℃，2.0 mm | 0.40 to 0.60 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.50 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | |
| Melt viscosity (260 ° C) | 215 | Pa·s | ISO 11443-A |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying temperature – Dry Air Dryer | 95 to 110 | °C | |
| Drying time – Dry Air Dryer | 4.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Suggested injection volume | 30 to 70 | % | |
| Temperature at the rear of the barrel | 230 to 240 | °C | |
| Temperature in the middle of the barrel | 235 to 245 | °C | |
| Front temperature of material barrel | 240 to 270 | °C | |
| Nozzle temperature | 265 to 275 | °C | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Back pressure | 5.00 to 15.0 | MPa | |
| Exhaust hole depth | 0.025 to 0.075 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |