| Partially hydrolysed grade Mowiol® and Kuraray Poval® are the trade name of the polyvinyl alcohols marketed by Kuraray. These are manufactured from polyvinyl acetate by alcoholysis using a continuous process. By varying the degree of polymerization of the polyvinyl acetate and its degree of hydrolysis (saponification), a number of different grades can be supplied. Our PVOH types are offered in a high standard purity showing especially “low ash and VOC contents”.&& |
| Product Description | |
|---|---|
| Supplier | Kuraray |
| Generic | PVOH |
| Material Status | Commercial: Active |
| Features | Biodegradable,Good bond,Block resin,Water soluble,Good coloring |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Apparent density | 0.40 to 0.60 | g/cm³ | DIN 53466 |
| Solution viscosity | 13 to 17 | mPa·s | DIN 53015 |
| PH value | 4.5 to 7.0 | DIN 19261 | |
| Ash Content | < 0.50 | % | |
| Ester content | 180 to 220 | mg KOH/g | DIN 53401 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Degree of Hydrolysis | 79 to 84 | % | |
| Residual Acetyl Content | 15 to 17 | % | |
| nonvolatile content | 95 | % | DIN 53189 |
| Methanol extractable | < 3.0 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4 % aqueous solution at 20 °C |
| 3. Calculated as Na2O |
| 4. 4 % solution in distilled water |
| 5. Saponification |
| 6. After 3 hours’ drying at 105 °C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |