| Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method. Black: A-1133 HS BK 324 Natural: A-1133 HS NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Low moisture absorption |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 233 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 13400 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 319 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 11600 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 280 | ℃ | ISO 75-2/Af |
| Melting temperature | 313 | ℃ | ISO 11357-3 |
| Vicat Softening Temp |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+15 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 3.20 mm | 39 | KV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.84mm | HB | UL-94 | |
| 1.5mm | HB | UL-94 | |
| 3.0mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.8 | kJ/m² | ISO 180-1A |
| Charpy Unnotch Impact strength | |||
| 23℃ | 73 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 9.5 | kJ/m² | ISO 179/1eA |
| Notched impact strength of cantilever beam | |||
| 23℃ | 49 | kJ/m² | ISO 180/1U |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | Hr | |
| Water content | 0.045 | % | |
| Injection temperature | |||
| Rear barrel temperature | 300-320 | °C | |
| Barrel front temperature | 310-330 | °C | |
| Mold temperature | 130 | °C | |
| Notes |
|---|
| 1. Limited to use by GMNA Powertrain in water baffles, use in any other application requires approval from GM. |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 20000 hr |
| 4. 5000 hr |
| 5. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 6. Transmittance for natural only. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |