| GELOY HRA170D resin is a PC-ASA blend with permanent antistatic behavior. It is typically used in applications that require antidust properties and high impact retention. GELOY HRA170D resin is typically used in various outdoor and indoor applications requiring superior heat aging properties and colour stability.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,High impact resistance,Good color stability,Antistatic property |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 8.5 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 30 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 8.0 | g/10min | ISO 1133 |
| Melt Volume Rate | ISO 1133 | ||
| 220℃，10 kg | 8.00 | cm³/10min | |
| 260℃，5 kg | 29.0 | cm³/10min | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 17 | kJ/m² | |
| 23℃ | 45 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 140 | J/m | ASTM D256 |
| 23℃ | 450 | J/m | ASTM D256 |
| -30℃ | 14 | kJ/m² | ISO 180-1A |
| 23℃ | 45 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 127 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 106 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 104 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 137 | ℃ | ISO 306/A50 |
| — | 138 | ℃ | ISO 306/A120 |
| B50 | 121 | ℃ | ISO 306 |
| B120 | 122 | ℃ | ISO 306/B120 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 77 | ISO 868 | |
| Rockwell hardness | |||
| Level L | 57 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 63.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 2160 | MPa | ASTM D638 |
| — | 2150 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 50.0 | MPa | ASTM D638 |
| yield | 54.0 | MPa | ASTM D638 |
| yield | 51.0 | MPa | ISO 527-2/5 |
| yield | 54.0 | MPa | ISO 527-2/50 |
| fracture | 58.0 | MPa | ASTM D638 |
| fracture | 59.0 | MPa | ASTM D638 |
| fracture | 65.0 | MPa | ISO 527-2/5 |
| fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ASTM D638 |
| yield | 130 | % | ISO 527-2/5 |
| yield | 5.0 | % | ISO 527-2/50 |
| fracture | 160 | % | ASTM D638 |
| fracture | 140 | % | ASTM D638 |
| fracture | 130 | % | ISO 527-2/50 |
| Bending modulus | 2100 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85.0 to 95.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |