3M™ Dyneon™ Perfluoroelastomer PFE 80Z

About
3M™ Dyneon™ PFE 80Z is a technically advanced peroxide curable perfluoroelastomer. This product is designed to have improved acid resistance and lower metal ion extractables, making it ideal for wet process electronics manufacturing such as semiconductor and flat panel display. It is classified as FFKM per ASTM D1418. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability. Features and Benefits Very low metal ion content with low extractables in a wide range of chemicals Ideal for wet chemical, fluid handling, cleaning and chemical etching processes and for semiconductor manufacturing Can be compounded for better acid resistance than PFE 90Z Upper use temperature of 200°C&&

About

3M™ Dyneon™ PFE 80Z is a technically advanced peroxide curable perfluoroelastomer. This product is designed to have improved acid resistance and lower metal ion extractables, making it ideal for wet process electronics manufacturing such as semiconductor and flat panel display. It is classified as FFKM per ASTM D1418. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability. Features and Benefits Very low metal ion content with low extractables in a wide range of chemicals Ideal for wet chemical, fluid handling, cleaning and chemical etching processes and for semiconductor manufacturing Can be compounded for better acid resistance than PFE 90Z Upper use temperature of 200°C&&

Product Description
Generic	PFE
Material Status	Commercial: Active
Features	Low extract,Low (to None) Ion Content,Solvent resistance,Heat Stabilized
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.00	g/cm³
Mooney viscosity
ML 1+10，121℃	80	MU

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	72		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength	11.0	MPa	ASTM D412
100% strain	4.79	MPa	ASTM D412
Tensile strain
fracture	230	%	ASTM D412
Compression deformation
200℃，70 hr	49	%
200℃，168 hr	69	%
MH	1.34	J
ML	0.203	J
t’50	1.1	min
t’90	2.7	min
ts2	48.0	sec

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	-35.0	℃

Supplementary information	Nominal value	Unit	Test method
Tr10	-2	℃

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.