| About |
|---|
| Mineral and glass fiber reinforced injection moulding grade is a heat stabilized and weather resistant grade. It has improved UV resistance and sink mark resistance. The combination of mineral and glass fibers result in a high performance, low warp and cost effective engineering thermoplatics. It exhibits high strength, good UV resistance, rigidity and good heat distortion temperatures. It has a relatively high resistance to creep under load. The heat stabilizer system extends its retention of properties at elevated temperatures. It has a good chemical resistance to greases, oils and hydrocarbons. The grade is generally recommended for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds, and all external parts exposed to the environment.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Weather resistance is good,Low warping,Good flexibility,Grease resistance,Solvent resistance,Heat Stabilized,Hydrocarbons |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Apparent density | 0.70 | g/cm³ | |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.90 | % | ASTM D570 |
| saturated | 5.7 | % | ASTM D570 |
| Balance, 50% RH | 1.6 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 181 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 11000 | MPa | ASTM D790 |
| bending strength | 290 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.5 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 202 | ℃ | ASTM D648 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Polymer Abbreviation | PA6-GF+MF40 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 80 to 95 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2,0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |