U-polymer L-1003PA

About
P series resins are resins succeeding the characteristics of the neat polymer, U-100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few transparent polymer alloys that have heat resistance. The heat-stable P-series resins have variations different in heat resistance in the range from 150 to 175°C. There are few transparent heat-resistant resins among super engineering plastics, and thus P series resins are valuable. The resins have favorable weather resistance, and in particular, the P- 1001 resin is approved by SAE Standard (J576 and J578) and FMVSS Standard (108). Making the most of these characteristics, the resins may be used, for example, as the lenses for automobile lamps. High flow-type resins, P-1001A, and P-3001S, are also available for thin molding products.&&

About

P series resins are resins succeeding the characteristics of the neat polymer, U-100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few transparent polymer alloys that have heat resistance. The heat-stable P-series resins have variations different in heat resistance in the range from 150 to 175°C. There are few transparent heat-resistant resins among super engineering plastics, and thus P series resins are valuable. The resins have favorable weather resistance, and in particular, the P- 1001 resin is approved by SAE Standard (J576 and J578) and FMVSS Standard (108). Making the most of these characteristics, the resins may be used, for example, as the lenses for automobile lamps. High flow-type resins, P-1001A, and P-3001S, are also available for thin molding products.&&

Product Description
Supplier	UNITIKA
Generic	多芳基化合物
Material Status	Commercial: Active
Features	Weather resistance is good,Good flexibility,High impact resistance,Good Dimensional Stability,Good liquidity,Optical performance,High Heat Resistance,Lubricating,Heat Stabilized,Amorphous
Availabilitys	North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.23	g/cm³	ASTM D792
Shrinkage rate
MD：3.0 mm	0.80	%	ASTM D955
Water absorption rate
24hr，3.18 mm	0.26	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
3.2mm	280	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	175	℃	ASTM D648
Linear coefficient of thermal expansion
MD	6.2E-5	1/℃	ASTM D696

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	2.0E+16	ohms·cm	ASTM D257
Dielectric strength	31	kV/mm	ASTM D149
Dielectric constant
1 MHz	2.70		ASTM D150
Dissipation factor
1 MHz	0.010		ASTM D150
Arc resistance	127	sec	ASTM D495

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	123		ASTM D785
tensile strength	70.0	MPa	ASTM D638
Tensile strain
fracture	60	%	ASTM D638
Bending modulus	2200	MPa	ASTM D790
bending strength	82.0	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.