3M™ Dyneon™ Fluoroplastic FEP FLEX6309Z

About
3M™ Dyneon™ Fluoroplastic FEP FLEX6309Z is a fully fluorinated copolymer comprising tetrafluoroethylene and hexafluoropropylene. It was developed mainly for wire and cable extrusion and features greatly enhanced flexibility and stress cracking behavior. Special Features Excellent dielectric properties High thermal stability Service temperature rating up to more than 200 °C Outstanding chemical resistance Wide processing window Greatly enhanced flex life properties Extremely low flammability (high LOI) Smooth surface Excellent anti-stick properties Low coefficient of friction Very high weathering and UV stability Improved mechanical properties&&

About

3M™ Dyneon™ Fluoroplastic FEP FLEX6309Z is a fully fluorinated copolymer comprising tetrafluoroethylene and hexafluoropropylene. It was developed mainly for wire and cable extrusion and features greatly enhanced flexibility and stress cracking behavior. Special Features Excellent dielectric properties High thermal stability Service temperature rating up to more than 200 °C Outstanding chemical resistance Wide processing window Greatly enhanced flex life properties Extremely low flammability (high LOI) Smooth surface Excellent anti-stick properties Low coefficient of friction Very high weathering and UV stability Improved mechanical properties&&

Product Description
Generic	FEP
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,No viscosity,Good flexibility,Low coefficient of friction,Copolymer,Solvent resistance,Heat Stabilized,High ESCR
Availabilitys	North America,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.14	g/cm³	ISO 12086
Melt Flow Rate
372℃，5.0kg	9.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	630	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	30.0	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	350	%	ISO 527-2

THERMAL	Nominal value	Unit	Test method
Melting temperature	255	℃	ISO 12086

Electrical performance	Nominal value	Unit	Test method
Dielectric strength
0.25 mm	65	kV/mm	ASTM D149
Dielectric constant			ASTM D150
23 ℃，1 MHz	2.05		ASTM D150
23 ℃，9.40 GHz	2.04		ASTM D150
Dissipation factor			ASTM D150
1 MHz	5.0E-4		ASTM D150
9.4 GHz	3.0E-4		ASTM D150

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Extreme oxygen index	> 95	%	ASTM D2863

Supplementary information	Nominal value	Unit	Test method
MIT flexural strength (double folds, 200.0 µ m)	110000		ASTM D2176

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	330	°C
Barrel 2 zone temperature	345	°C
Barrel 3 zone temperature	360	°C
Barrel 4 zone temperature	370	°C
Barrel 5 zone temperature	385	°C
Nozzle temperature	395	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.