| About |
|---|
| 50% glass fiber reinforced, Polyamide 612 compound with high strength after conditioning (available with different kinds of heat stabilization systems)&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA612 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Solvent resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.90 | % | |
| Viscosity (H2SO4 (sulfuric acid)) | 110 | cm³/g | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 15600 | MPa | |
| tensile strength | |||
| fracture | 230 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | |
| Bending modulus | |||
| 23℃ | 14000 | MPa | |
| bending strength | |||
| 3.60% strain, 23 ℃ | 350 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | 14 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -40℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 218 | ℃ | |
| 1.8 MPa, unannealed | 205 | ℃ | |
| Vicat Softening Temp | |||
| — | 216 | ℃ | |
| — | 208 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | |
| Volume resistivity | > 1.0E+13 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | < 50 | mm/min | |
| 2.0 mm | < 50 | mm/min | |
| Flammability level | |||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| Glowing wire flammability index | |||
| 1.5 mm | 650 | ℃ | |
| 3.0 mm | 650 | ℃ | |
| Igniting temperature of the hot wire | |||
| 1.5 mm | 700 | ℃ | |
| 3 mm | 700 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 to 0.10 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |