| High flow PPO+PA. Power distribution box applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 97 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.2 to 1.4 | % | |
| TD：3.2 mm | 1.1 to 1.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1950 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 64.0 | MPa | ASTM D638 |
| yield | 69.0 | MPa | ISO 527-2/50 |
| fracture | 62.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 11 | % | ASTM D638 |
| fracture | 40 | % | ASTM D638 |
| fracture | 39 | % | ISO 527-2/5 |
| Bending modulus | |||
| 100 mm span | 2350 | MPa | ASTM D790 |
| — | 2700 | MPa | ISO 178 |
| bending strength | |||
| Yield, 100 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 110 | J/m | ASTM D256 |
| 23℃ | 260 | J/m | ASTM D256 |
| -40℃ | 13 | kJ/m² | ISO 180-1A |
| -20℃ | 15 | kJ/m² | ISO 180-1A |
| 23℃ | 21 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 770 | J/m | |
| 23℃ | 850 | J/m | |
| Dart impact equipped with measuring instruments | |||
| -30℃，Total Energy | 15.0 | J | |
| 23℃，Total Energy | 43.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 190 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 202 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 4.0 mm, 64 mm span | 187 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 83.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 170 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 78.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 212 | ℃ | ASTM D1525 7 |
| B50 | 203 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 1.2E-4 | 1/℃ | |
| TD：-40~40℃ | 1.4E-4 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 to 105 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Recommended injection volume | 30 to 50 | % | |
| Barrel rear temperature | 255 to 295 | °C | |
| Barrel middle temperature | 260 to 295 | °C | |
| Barrel front temperature | 265 to 295 | °C | |
| Nozzle temperature | 270 to 295 | °C | |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 65 to 95 | °C | |
| Back pressure | 0.300 to 1.40 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.013 to 0.038 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.10 in/min |
| 5. 0.079 in/min |
| 6. 80*10*4 mm |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |