| About |
|---|
| Solef® 11010 PVDF is a medium-viscosity flexible PVDF copolymer resin and is typically processed by extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Material Status | Commercial: Active |
| Features | V-0,Good flexibility,Copolymer |
| Availabilitys | Europe,Africa & Middle East ,Asia Pacific,North America,Latin America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，5.0kg | 4.0 to 8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 2.0 to 3.0 | % | |
| Water Absorption | |||
| 23℃，24hr | < 0.040 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second, 2.00 mm | 70 to 75 | ASTM D2240 | |
| Tensile Modulus | |||
| 23℃，2 mm | 800 to 1200 | MPa | ASTM D638 |
| Tensile Strength | |||
| Broken BRK, 23 ℃, 2 mm | 20.0 to 40.0 | MPa | ASTM D638 |
| Yield yld, 23 ℃, 2 mm | 20.0 to 35.0 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK, 23 ℃, 2 mm | 200 to 600 | % | ASTM D638 |
| Yield yld, 23 ℃, 2 mm | 10 to 12 | % | ASTM D638 |
| Frictional coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.15 to 0.35 | ASTM D1894 | |
| With oneself – static | 0.20 to 0.40 | ASTM D1894 | |
| Taber Abrasion | |||
| 1000 cycles, 1000 g, CS-10 wheels | 5.00 to 15.0 | mg | ASTM D4060 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃，4mm | 150 to 250 | J/m | ASTM D6110 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass Transition Temperature | -35.0 | ℃ | ASTM D4065 |
| Vicat Softening Temperature | 90.0 to 105 | ℃ | ASTM D1525 5 |
| Melting temperature | 158 to 162 | ℃ | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | |||
| DSC | 115 to 130 | ℃ | ASTM D3418 |
| Coeff. of linear thermal expansion | |||
| MD：0~40℃ | 1.8E-4 | 1/℃ | ASTM D696 |
| Specific Heat | ASTM E968 | ||
| 23℃ | 1200 | J/kg/℃ | ASTM E968 |
| 100℃ | 1600 | J/kg/℃ | ASTM E968 |
| Thermal conductivity | |||
| 23℃ | 0.19 | W/m/K | ASTM C177 |
| Crystallization Heat | 30.0 to 40.0 | J/g | ASTM D3417 |
| Heat of Fusion | 35.0 to 40.0 | J/g | ASTM D3417 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistance | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | |||
| 23 ℃，1 mm | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23 ℃，1 MHz | 7.00 to 10.0 | ASTM D150 | |
| Dissipation Factor | |||
| 23℃，1 MHz | 0.20 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.10 mm | V-0 | UL 94 | |
| Extreme oxygen index | |||
| 3.0 mm | 44 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 0.039 in/min |
| 3. Type IV, 2.0 in/min |
| 4. 2 m/s |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |