| About |
|---|
| Siltem 1600 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity. It is an amber colored transparent material that can be selfcolored and easily processed on conventional equipment. The material may also have a fit in flexible profiles or injection molded parts.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low smoke,Halogen free,Flame Characteristics,Low toxicity,Copolymer,V-0 |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 295℃，6.60kg | 8.6 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.86 to 1.0 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.58 | % | ISO 62 |
| 23℃，24hr | 0.58 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 72 | ASTM D2240 | |
| Tensile modulus | 1400 | MPa | ASTM D638 |
| Tensile modulus | 1380 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 41.0 | MPa | ISO 527-2/50 |
| fracture | 40.0 | MPa | ASTM D638 |
| yield | 42.0 | MPa | ISO 527-2/50 |
| yield | 43.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 74 | % | ISO 527-2/50 |
| fracture | 64 | % | ASTM D638 |
| yield | 10 | % | ISO 527-2/50 |
| yield | 10 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 50 mm span | 1250 | MPa | ASTM D790 |
| — | 1250 | MPa | ASTM D790 |
| Bending modulus | 1250 | MPa | ISO 178 |
| bending strength | 48.0 | MPa | ASTM D790 |
| Yield, 50 mm span | 48.0 | MPa | ASTM D790 |
| bending strength | 55.0 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 50.0 | mg | ASTM D1044 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 410 | J/m | ASTM D256 |
| -30℃ | 25 | kJ/m² | ISO 180-1A |
| 23℃ | 36 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 80.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 144 | ℃ | ISO 75-2/Bf |
| Glass transition temperature | 195 | ℃ | DSC |
| Vicat Softening Temp | |||
| B120 | 167 | ℃ | ISO 306/B120 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 100 Hz | 3.14 | ASTM D150 | |
| 100 kHz | 3.05 | ASTM D150 | |
| 1 MHz | 3.02 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 100 Hz | 0.014 | ASTM D150 | |
| 100 kHz | 6.4E-3 | ASTM D150 | |
| 1 MHz | 5.5E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 | |
| Extreme oxygen index | 48 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 105 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 310 to 320 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 310 to 320 | °C | |
| Nozzle temperature | 310 to 320 | °C | |
| Processing (melt) temperature | 310 to 320 | °C | |
| Mold temperature | 105 to 115 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Drying temperature | 110 to 130 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 270 to 310 | °C | |
| Barrel 3 zone temperature | 280 to 320 | °C | |
| Barrel 5 zone temperature | 290 to 330 | °C | |
| Melt temperature | 290 to 330 | °C | |
| Nozzle temperature | 290 to 330 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Type 1A |
| 7. at Yield |
| 8. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |