| About |
|---|
| 40% Glass fiber reinforced / Low-flash and toughness&& |
| Product Description | |
|---|---|
| Supplier | TOSOH |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good flexibility,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.64 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.80 | % | ISO 294-4 |
| MD | 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | < 0.020 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 176 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.5 | % | ISO 527-2 |
| Bending modulus | 14700 | MPa | ISO 178 |
| bending strength | 275 | MPa | ISO 178 |
| Tensile Weld Strength | 60.0 | MPa | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 82 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 260 | ℃ | ISO 75-2/A |
| Melting temperature | 285 | ℃ | Internal Method |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric strength | 16 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 3.90 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 1.4E-3 | IEC 60250 | |
| Compared to the leakage tracing index | PLC 4 | UL 746 | |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Rod flow length | 175 | mm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 150 | °C | |
| Drying time | 2.0 to 5.0 | hr | |
| Barrel rear temperature | 270 to 300 | °C | |
| Barrel middle temperature | 270 to 300 | °C | |
| Nozzle temperature | 290 to 330 | °C | |
| Mold temperature | 135 to 150 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |