| About |
|---|
| Sekisui PVC HA-36F is a Polyvinyl Chloride product. It is available in Asia Pacific. Primary characteristic: heat resistant.&& |
| Product Description | |
|---|---|
| Supplier | Sekisui |
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | Good flexibility,High elastic,Renewable resources,Food contact compliance,Good tear strength,Solvent resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | JIS K7112 |
| Apparent density | 0.50 to 0.60 | g/cm³ | JIS K6720-2 |
| K-Value | 61.0 | JIS K6720-2 | |
| Chlorine Content | 64.0 | wt% | ISO 1158 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 59.0 | MPa | JIS K7113 |
| Tensile strain | |||
| fracture | 80 | % | JIS K7113 |
| Bending modulus | 2750 | MPa | JIS K7171 |
| bending strength | 86.0 | MPa | JIS K7171 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 29 | kJ/m² | JIS K7111 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 | ℃ | JIS K7207 |
| 1.8 MPa, unannealed | 85.0 | ℃ | JIS K7191-1 |
| Vicat Softening Temp | 104 | ℃ | JIS K7206 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 to 7.5E-5 | 1/℃ | ASTM D696 |
| Heat loss | < 0.3 | wt% | JIS K6720-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | |
| Dielectric strength | 47 to 63 | kV/mm | |
| Dielectric constant | |||
| 60 Hz | 3.08 | ||
| 1 MHz | 3.20 to 3.60 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| temperature | |||
| Flex | 86 | ℃ | JIS K6745 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% RH |
| 3. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |