| About |
|---|
| LL 1002AY is a C4 Ziegler Natta LLDPE for Low Voltage power cable and Telecom jacketing. The grade contains a higher level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Carbon Black or UV stabilizer should be added to meet cable jacketing specifications.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Negative |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric constant | |||
| 60 Hz | 2.17 | ASTM D150 | |
| Dissipation factor | |||
| 60 Hz | < 1.0E-4 | ASTM D150 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 48 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 12.0 | MPa | ASTM D638 |
| fracture | 17.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 16 | % | ASTM D638 |
| fracture | 700 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 300 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |