| About |
|---|
| Description BI300 is a high isotactic Block Copolymer which has higher crystallinity, compared to general PP. Due to high crystalline nature & optimum rubber design, BI300 has an excellent property balance between high stiffness and impact strength. Films made from this grade provide high heat resistance and superior mechanical strength, thus this grade is highly suited to retort pouch film application. Characteristics Good balance physical property between stiffness & impact strength Punch resistance Heat resistance High transparency Applications Retort pouch, Cast film&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | HC PP |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High impact resistance,Good Dimensional Stability,Good disinfection,Crystal,High Heat Resistance,Block Copolymer,low-temperature impact resistance,High pressure heat resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 60 | µm | |
| tensile strength | ASTM D882 | ||
| fracture | 23.5 | MPa | ASTM D638 |
| MD, yield, 60 µ m | 22.6 | MPa | ASTM D882 |
| TD, yield, 60 µ m | 20.6 | MPa | ASTM D882 |
| MD, fracture, 60 µ m | 53.0 | MPa | ASTM D882 |
| TD, fracture, 60 µ m | 36.3 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| fracture | 500 | % | ASTM D638 |
| MD, fracture, 60 µ m | 700 | % | ASTM D882 |
| TD, fracture, 60 µ m | 700 | % | ASTM D882 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 0℃ | 29 | J/m | ASTM D256 |
| 5℃ | 39 | J/m | ASTM D256 |
| 23℃ | 64 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 110 | ℃ | ASTM D648 |
| Vicat Softening Temp | 155 | ℃ | ASTM D1525 3 |
| Melting temperature | 163 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 60 µm | 28 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 81 | ASTM D785 | |
| Bending modulus | 1470 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |