Toppyl SP 2000 B

About
Toppyl SP 2000 B is a fully formulated seal peel solution especially developed for the blown film technology. This product has been designed to offer a peelable seal to PE substrates or to seal & peel against itself and is suitable for non-sterilisable applications. Toppyl SP 2000B is a solution created to replace completely the sealing layer in a coextruded film. It provides a constant easy-opening force over a wide sealing temperature window and is readily processable on conventional equipment in both mono and co-extruded structures. EU and FDA compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications.&&

About

Toppyl SP 2000 B is a fully formulated seal peel solution especially developed for the blown film technology. This product has been designed to offer a peelable seal to PE substrates or to seal & peel against itself and is suitable for non-sterilisable applications. Toppyl SP 2000B is a solution created to replace completely the sealing layer in a coextruded film. It provides a constant easy-opening force over a wide sealing temperature window and is readily processable on conventional equipment in both mono and co-extruded structures. EU and FDA compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications.&&

Product Description
Supplier	LyondellBasell
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	Good heat sealing,Food contact compliance,Hypocrystalline,Good melt strength,Broad Seal Range,Good tear strength
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.912	g/cm³	ISO 1183
Melt Flow Rate	2.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
friction coefficient	0.25		ASTM D1894

film	Nominal value	Unit	Test method
Secant modulus
MD	185	MPa	ASTM D882
tensile strength			ASTM D882
MD, yield	9.00	MPa	ASTM D882
MD, fracture	28.0	MPa	ASTM D882
Tensile strain
MD, fracture	670	%	ASTM D882

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp
A50	90.0	℃	ISO 306/A50
Melting temperature	110	℃	DSC

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	170 to 230	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.