| LNP™ LUBRICOMP™ MFL36S compound LNP LUBRICOMP MFL36S is a compound based on Polypropylene resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound MFXL-4036 HS Product reorder name: MFL36S&&LNP™ LUBRICOMP™ MFL36S compound LNP LUBRICOMP MFL36S is a compound based on Polypropylene resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound MFXL-4036 HS Product reorder name: MFL36S&&LNP™ LUBRICOMP™ MFL36S compound LNP* Lubricomp* MFL36S is a compound based on Polypropylene resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound MFXL4036HS Product reorder name: MFL36S&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.40 | % | ASTM D995 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 72 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.9 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 7600 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 117 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 5870 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 91 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 590 | J/m | ASTM D4812 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 195-205 | °C | |
| Central temperature of the barrel | 215-225 | °C | |
| Barrel front temperature | 240-250 | °C | |
| Mold temperature | 30-50 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |