| BC918CF is a heterophasic copolymer. BC918CF is a high crystalline copolymer film resin. This grade is suitable for the manufacturing of unoriented films on cast lines, conventional blown film lines with air cooling as well as roll stack process for thermoformable films/sheets. CAS-No. 9010-79-1&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | HC PP |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good flexibility,High purity,Crystal,Good tear strength,Copolymer,low-temperature impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 23 ℃, injection molding | 1400 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-3 | ||
| MD，50 µm | 1150 | MPa | ISO 527-3 |
| TD，50 µm | 980 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m | 570 | % | ISO 527-3 |
| TD, fracture, 50 µ m | 530 | % | ISO 527-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20 ℃, injection molding | 1.2 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 35 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 168 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，50 µm | 95 | ASTM D2457 | |
| Haze | |||
| 50 µm | 4.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |