| Description: Eco Solution GP300 is a PLA (polyactide) based alloy with PBS (Poly Butylene Succinate) and is certified as a biodegradable resin and meet ASTM D6400, EN13432. The processibility and toughness are greatly improved and thus can be leaded in INJECTION process easily. Applications Superior injection material can work friendly with conventional INJECTOIN Machin&& |
| Product Description | |
|---|---|
| Generic | PLA+PBS |
| Material Status | Commercial: Negative |
| Features | Biodegradable,Compostable |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 14 to 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.1 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 49 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 88.3 | ℃ | ASTM D648 |
| Melting temperature | 113 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 88 | ASTM D2240 | |
| Tensile modulus | 2270 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 35.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 7.4 | % | ASTM D638 |
| Bending modulus | 1480 | MPa | ASTM D790 |
| bending strength | |||
| yield | 50.3 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |