| About |
|---|
| Alkathene XDS34 is a low density polyethylene designed for a variety of heavy gauge (70 – 200µm) film applications. Alkathene XDS34 does not contain any additives. Film Extrusion: Alkathene XDS34 is intended for applications such as sacks, palletwrap, shrink film and a variety of industrial films requiring heavy gauge film.&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Food contact compliance |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 100 | µm | |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 100 µ m, blow molded film | 130 | MPa | ASTM D882 |
| 2% secant, TD: 100 µ m, blow molded film | 140 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 100 µ m, blow molded film | 11.0 | MPa | ASTM D882 |
| TD, yield, 100 µ m, blow molded film | 10.0 | MPa | ASTM D882 |
| MD, fracture, 100 µ m, blow molded film | 26.0 | MPa | ASTM D882 |
| TD, fracture, 100 µ m, blow molded film | 23.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 100 µ m, blow molded film | 610 | % | ASTM D882 |
| TD, fracture, 100 µ m, blow molded film | 820 | % | ASTM D882 |
| Drop hammer impact | |||
| 100 µ m, blow molded film | 330 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 100 µ m, blow molded film | 530 | g | ASTM D1922 |
| TD: 100 µ m, blow molded film | 690 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 100 µ m, blow molded film | 71 | ASTM D2457 | |
| Haze | |||
| 100 µ m, blow molded film | 8.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.79 in/min |
| 3. 20 in/min |
| 4. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |