| RIALENE P 100 SGF20 ST F V-0 natural is a semi-crystalline thermoplastic construction material based on polypropylene (PP), reinforced with 20 % special glass fiber (SGF) which is optimized linked to the polymer matrix. RIALENE P 100 SGF20 ST F V-0 natural will be processed by injection molding and has halogen- and heavy metal-free fire protection equipment. RIALENE P 100 SGF20 ST F V-0 natural is characterized by the following properties: UL 94 V-0 listed at 1.5 mm Conform to GWIT 800 °C at 1.5 mm excellent rigidity and strength with good elongation behavior excellent thermo-mechanical properties halogen- and heavy metal-free flame retardants (conform to WEEE and RoHS) very low smoke density no corrosion during processing&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Halogen free,Flame Characteristics,Hypocrystalline,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 5.40 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.40 to 0.55 | % | ISO 294-4 |
| MD | 0.25 to 0.35 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6100 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/5 | ||
| yield | 80.0 | MPa | ISO 527-2/5 |
| fracture | 78.0 | MPa | ISO 527-2/5 |
| Tensile strain | ISO 527-2/5 | ||
| yield | 4.0 | % | ISO 527-2/5 |
| fracture | 4.4 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 42 | kJ/m² | ISO 179/1eU |
| 23℃ | 44 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 147 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 143 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric strength | 41 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1.5 mm | 800 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.030 | % | |
| Hopper temperature | 50 to 70 | °C | |
| Barrel rear temperature | 220 to 230 | °C | |
| Barrel middle temperature | 220 to 240 | °C | |
| Barrel front temperature | 220 to 250 | °C | |
| Nozzle temperature | 220 to 250 | °C | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |