| NORYL V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 1.0 mm. NORYL V02570 is may be an excellent material candidate for application requiring electrically insulating properties, low warpage and thin wall flame resistance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Low warping,Good Dimensional Stability,Good Electrical Properties,Halogen free,Flame Characteristics,Insulation |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 12 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.30 to 0.50 | % | |
| MD：3.2 mm | 0.30 to 0.50 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.25 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| -30℃ | 30 | kJ/m² | |
| 23℃ | 30 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 35 | J/m | |
| 23℃ | 35 | J/m | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 25 | kJ/m² | |
| 23℃ | 25 | kJ/m² | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 9.00 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 155 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 148 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 145 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| — | 165 | ℃ | ASTM D1525 13 |
| B50 | 160 | ℃ | ISO 306 |
| B120 | 167 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 123~127℃ | 通过 | ||
| 155℃ | 通过 | ||
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 4.5E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 5.0E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.28 | W/m/K | ISO 8302 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 0.8 mm in oil | 33 | kV/mm | |
| 1.6 mm in oil | 26 | kV/mm | |
| 3.2 mm in oil | 18 | kV/mm | |
| Relative permittivity | |||
| 50 Hz | 3.00 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 2.90 | ||
| Dissipation factor | |||
| 50 Hz | 5.0E-3 | ||
| 60 Hz | 5.0E-3 | ||
| 1 MHz | 4.0E-3 | ||
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 1 | UL 746 | |
| High voltage arc ignition resistance index (HVAR) (PLC) | PLC 3 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 825 | ℃ | |
| 2 mm | 775 | ℃ | |
| 3 mm | 775 | ℃ | |
| Extreme oxygen index | 32 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 115 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 3600 | MPa | ASTM D638 |
| — | 4700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 75.0 | MPa | ASTM D638 |
| yield | 73.0 | MPa | ISO 527-2/5 |
| fracture | 75.0 | MPa | ASTM D638 |
| fracture | 73.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| yield | 4.0 | % | ISO 527-2/5 |
| fracture | 4.0 | % | ASTM D638 |
| fracture | 4.0 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 3800 | MPa | ASTM D790 |
| — | 3800 | MPa | ISO 178 |
| bending strength | |||
| — | 123 | MPa | ISO 178 |
| — | 115 | MPa | ISO 178 |
| Yield, 50 mm span | 120 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 270 to 290 | °C | |
| Barrel middle temperature | 290 to 310 | °C | |
| Barrel front temperature | 310 to 330 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Processing (melt) temperature | 290 to 330 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.20 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Break |
| 8. at Yield |
| 9. 80*10*4 sp=62mm |
| 10. 80*10*4 mm |
| 11. 120*10*4 mm |
| 12. Rate A (50°C/h), Loading 2 (50 N) |
| 13. Approximate Maximum |
| 14. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |