| PRODUCTS FOR GASKETS These are specially developed TPUs for manufacturing hydraulic gaskets or any other application where at high compression set, resistance to oils and/or high temperatures, is required. Two products based on polycaprolactone (2202-95A and 107- 93A) plus one based on Ether (2203-93A) belong to this group depending on the application.&& |
| Product Description | |
|---|---|
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good wear resistance,Good compressive strength,Solvent resistance |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | DIN 53479 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | DIN 53504 | ||
| 50% | 9.00 | MPa | DIN 53504 |
| 100% | 11.2 | MPa | DIN 53504 |
| 300% | 21.4 | MPa | DIN 53504 |
| tensile strength | |||
| fracture | 51.1 | MPa | DIN 53504 |
| Tensile strain | |||
| fracture | 460 | % | DIN 53504 |
| tear strength | 80 | N/mm² | DIN 53515 |
| Vicat Softening Temp | 145 | ℃ | ISO 306 |
| Compression deformation | |||
| 23℃，70 hr | 16 | % | DIN 53517 |
| 70℃，22 hr | 28 | % | DIN 53517 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 92 | DIN 53505 | |
| Bending modulus | 45.0 | ISO 178 | |
| Wear amount | 30.0 | mm³ | DIN 53516 |
| Tear resistance | 80.0 | MPa | DIN 53515 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 190 | °C | |
| Barrel 2 zone temperature | 195 | °C | |
| Barrel 3 zone temperature | 200 | °C | |
| Nozzle temperature | 195 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |