| About |
|---|
| AvaSpire® AV-621 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-621. It offers better dimensional stability and warp resistance than 30% carbon fiber reinforced PEEK. The AV-621 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-621 based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK including chemical resistance, fatigue resistance, and long term thermal oxidative stability. The excellent balance of properties of AV-621 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, and chemical processing. This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-621 CF30 is very similar to that of 30% CF reinforced PEEK. The lower melt flow of AV-621 CF30 is well suited for extrusion applications while offering a similar property profile to AV-651 CF30.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| — | 69 | J/m | ASTM D256 |
| — | 9.6 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | |||
| — | 640 | J/m | ASTM D4812 |
| — | 39 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.2 mm | 210 | ℃ | ASTM D648 |
| Glass transition temperature | 160 | ℃ | ASTM D3418 |
| Melting peak temperature | 340 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD：-50~50℃ | 5.0E-6 | 1/℃ | ASTM E831 |
| specific heat | DSC | ||
| 50℃ | 1350 | J/kg/℃ | DSC |
| 200℃ | 1810 | J/kg/℃ | DSC |
| Thermal conductivity coefficient | 0.35 | W/m/K | ASTM E1530 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 101 | ASTM D785 | |
| Tensile modulus | |||
| — | 17200 | MPa | ASTM D638 |
| — | 23300 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 196 | MPa | ISO 527-2/1A/5 |
| — | 181 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.2 | % | ASTM D638 |
| fracture | 2.2 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| — | 15100 | MPa | ASTM D790 |
| — | 21300 | MPa | ISO 178 |
| bending strength | |||
| — | 276 | MPa | ASTM D790 |
| — | 296 | MPa | ISO 178 |
| compressive strength | 152 | MPa | ASTM D695 |
| shear strength | 91.0 | MPa | ASTM D732 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：3.2 mm | 0.0 to 0.20 | % | ASTM D955 |
| TD：3.2 mm | 0.90 to 1.1 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 400℃，1000 sec^-1 | 790 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 366 | °C | |
| Barrel middle temperature | 371 | °C | |
| Barrel front temperature | 377 | °C | |
| Nozzle temperature | 382 | °C | |
| Processing (melt) temperature | 366 to 388 | °C | |
| Mold temperature | 149 to 177 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 5″ x 0.5″ x 0.125″ bars |
| 3. 0.20 in/min |
| 4. 2 hours at 200°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |