| LNP* Thermocomp* ZKC06 is a compound based on PPO resin containing Mineral Filler, Impact Modifier. Added features of this material include: high dielectric constant (Dk), extremely low dissipation factor (Df), good ductility, and good thermal performance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+SEBS |
| Material Status | Commercial: Negative |
| Features | High impact resistance,Ductility,Heat Resistance, Good,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792，ISO 1183 |
| Melt Flow Rate | ASTM D1238 | ||
| 300℃，10.0kg | 36 | g/10min | ASTM D1238 |
| 300℃，5.0kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | ISO 1133 | ||
| 300℃，10 kg | 30.0 | cm³/10min | ISO 1133 |
| 300℃，5 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.60 to 0.80 | % | ISO 294-4 |
| MD：24 hrs | 0.60 to 0.80 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.030 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2530 | MPa | ASTM D638 |
| — | 2490 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ASTM D638 |
| yield | 56.0 | MPa | ISO 527-2/50 |
| fracture | 46.0 | MPa | ASTM D638 |
| fracture | 49.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 8.7 | % | ASTM D638 |
| yield | 7.9 | % | ISO 527-2/50 |
| fracture | 14 | % | ASTM D638 |
| fracture | 16 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2350 | MPa | ASTM D790 |
| — | 2620 | MPa | ISO 178 |
| bending strength | |||
| — | 95.0 | MPa | ISO 178 |
| — | 93.0 | MPa | ISO 178 |
| Yield, 50 mm span | 85.0 | MPa | ASTM D790 |
| Fracture, 50 mm span | 83.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -20℃ | 150 | J/m | ASTM D256 |
| 23℃ | 280 | J/m | ASTM D256 |
| -20℃ | 13 | kJ/m² | ISO 180-1A |
| 23℃ | 30 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 173 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 173 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 154 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 155 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~150℃ | 6.1E-5 | 1/℃ | ASTM E831 |
| TD：-40~150℃ | 8.7E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | Internal Method | ||
| 1.10 GHz | 3.56 | Internal Method | |
| 1.9 GHz | 3.57 | Internal Method | |
| 5.00 GHz | 3.57 | Internal Method | |
| 10.0 GHz | 3.58 | Internal Method | |
| Dissipation factor | Internal Method | ||
| 1.1 GHz | 9.0E-4 | Internal Method | |
| 1.9 GHz | 1.1E-3 | Internal Method | |
| 5 GHz | 1.9E-3 | Internal Method | |
| 10 GHz | 2.2E-3 | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.0 to 3.0 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 105 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Barrel rear temperature | 280 to 285 | °C | |
| Barrel middle temperature | 290 to 295 | °C | |
| Barrel front temperature | 300 to 305 | °C | |
| Nozzle temperature | 290 to 295 | °C | |
| Processing (melt) temperature | 295 to 305 | °C | |
| Mold temperature | 90 | °C | |
| Back pressure | 9.00 | MPa | |
| Screw speed | 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Break |
| 7. at Yield |
| 8. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |