| Unreinforced, Toughened, PPA, High Performance Polyamide&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | HB,Heat Stabilized |
| Availabilitys | Latin America,Africa & Middle East ,Asia Pacific,Europe,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Molding shrinkage | |||
| Parallel | 0.8 | % | ISO 294-4 |
| Normal | 0.9 | % | ISO 294-4 |
| Moisture Absorption | 1.9 | % | ISO 62 |
| Water Absorption | 6.3 | % | ISO 62 |
| Density | 9.44 | lb/gal | ISO 1183 |
| Density of melt | 60.6 | lb/ft³ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 2208 | MPa | ISO 527 |
| Wet Cond | 2277 | MPa | ISO 527 |
| Tensile Stress | |||
| Yield yld, dry dry dry | 68.31 | MPa | ISO 527 |
| Yield yld, wet cond | 68.31 | MPa | ISO 527 |
| Tensile Strain | |||
| Yield yld, dry dry dry | 5.5 | % | ISO 527 |
| Yield yld, wet cond | 4.4 | % | ISO 527 |
| Broken BRK, dry dry | 14 | % | ISO 527 |
| Broken BRK, wet Cond | 10 | % | ISO 527 |
| Flexural Modulus | |||
| Dry | 2104.5 | MPa | ISO 178 |
| Wet Cond | 2201.1 | MPa | ISO 178 |
| Poisson’s ratio | |||
| Dry | 0.39 | ||
| Wet Cond | 0.39 | ||
| Frictional coefficient | 0.4 | ASTM D1894 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23 ℃, dry | NB | kJ/m² | ISO 179/1eU |
| 23 ℃, moist cond | NB | kJ/m² | ISO 179/1eU |
| -30 ℃, dry | NB | kJ/m² | ISO 179/1eU |
| -30 ℃, moist cond | NB | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | 75.6 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| 23 ℃, dry | 74.97 | KJ/m² | ISO 180/1A |
| -30 ℃, moist cond | 17.98 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10 ℃/min | 300 | ℃ | ISO 11357-3 |
| First heat | 300 | ℃ | ISO 11357-3 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 127 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 138 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel, -40-23 ℃ | 0.5 | E-4/°F | ISO 11359-2 |
| Parallel | 0.5 | E-4/°F | ISO 11359-2 |
| Parallel, 55-160 ℃ | 0.506 | E-4/°F | ISO 11359-2 |
| Normal, -40-23 ℃ | 0.4 | E-4/°F | ISO 11359-2 |
| Normal | 0.467 | E-4/°F | ISO 11359-2 |
| Normal, 55-160 ℃ | 0.478 | E-4/°F | ISO 11359-2 |
| Thermal conductivity | |||
| Flowing flow | 0.27 | W/m/K | ISO 22007-2 |
| Melt | 0.18 | W/m/K | |
| Specification of Melt Heat Capacity of Melt | 0.835 | BTU/(lb·F) | |
| Relative Temperature Index (RTI) | |||
| Electrical | |||
| 0.75 mm | 65 | ℃ | UL-746B |
| 1.5 mm | 65 | ℃ | UL-746B |
| 3.0 mm | 65 | ℃ | UL-746B |
| Impact | |||
| 0.75 mm | 65 | ℃ | UL-746B |
| 1.5 mm | 65 | ℃ | UL-746B |
| 3.0 mm | 65 | ℃ | UL-746B |
| Strength | |||
| 0.75 mm | 65 | ℃ | UL-746B |
| 1.5 mm | 65 | ℃ | UL-746B |
| 3.0 mm | 65 | ℃ | UL-746B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.6 mm | HB | calss | UL 94 |
| 0.8 mm | HB | calss | UL 94 |
| FMVSS flame retardant rating | B | ISO 3795 | |
| Burning Speed | <80 | in/min | ISO 3795 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E13 | ohm·m | IEC 62631-3-1 |
| Surface Resistivity | >1E15 | ohm | IEC 62631-3-2 |
| Compared Tracking Index | 600 | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 320 to 330 | ℃ | |
| Melt Temperature, Optimal | 325 | ℃ | |
| Mold Temperature | 80 to 120 | ℃ | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |