| HAB8740 is a high flow and high Impact PBT/ABS alloy resin, offering medium heat resistance,excellent normal and low temperature impact strength and chemical resistance.HAB8740 is recommended for automobile parts, office appliance, electrical and electronic components.&& |
| Product Description | |
|---|---|
| Supplier | KumhoSunny |
| Generic | ABS+PBT |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Heat Resistance, Good,Solvent resistance,low-temperature impact resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.13 | g/cm³ | ASTM D792 |
| — | 1.17 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 20 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 18 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.80 | % | ASTM D955 |
| — | 0.50 to 0.80 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| — | 47.0 | MPa | ASTM D638 |
| — | 50.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 150 | % | ASTM D638 |
| Bending modulus | |||
| — | 1700 | MPa | ASTM D790 |
| — | 2000 | MPa | ISO 178 |
| bending strength | |||
| — | 65.0 | MPa | ASTM D790 |
| — | 65.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 23 | kJ/m² | ISO 179 |
| 23℃ | 48 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 700 | J/m | ASTM D256 |
| 23℃ | 45 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 95.0 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Barrel rear temperature | 225 to 240 | °C | |
| Barrel middle temperature | 230 to 260 | °C | |
| Barrel front temperature | 230 to 260 | °C | |
| Nozzle temperature | 230 to 260 | °C | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Back pressure | 0.200 to 0.800 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 120°C/h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |