| About |
|---|
| ARLEN™ CH230N (Dry) ARLEN™ CH230N is a Polyamide 6T (Nylon 6T) material filled with 30% glass fiber. It is available in North America. Important attributes of ARLEN™ CH230N are: Flame Rated Flame Retardant Typical application of ARLEN™ CH230N: Electrical/Electronic Applications&&ARLEN™ CH230N ARLEN™ CH230N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ CH230N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating. Features: High dimensional stability High melting point High rigidity Minimum water absorption Good chemical and heat resistance Flame retardant Applications: Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.&& |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | PA 6T |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ASTM D792 |
| Molding shrinkage | |||
| MD | 0.40 | % | ASTM D995 |
| TD | 0.80 | % | ASTM D995 |
| Water Absorption | |||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 290 | ℃ | ASTM D648 |
| Coeff. of linear thermal expansion | |||
| MD | 3.0E-5 | 1/℃ | ASTM D696 |
| TD | 6.0E-5 | 1/℃ | ASTM D696 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1.0E+15 | Ω.cm | ASTM D257 |
| Insulation Strength | |||
| 25 | KV/mm | ASTM D149 | |
| Dielectric Constant | |||
| 23℃ | 4.00 | 1 MHz | ASTM D150 |
| Dissipation Factor | |||
| 23℃ | 0.01 | 1 MHz | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.75mm | V-0 | UL 94 | |
| 1.50mm | V-0 | UL 94 | |
| 3.00mm | V-0 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23℃ | 80 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 95 | M 级 | ASTM D785 |
| Tensile Strength | |||
| 23℃ | 160 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK, 23 ℃ | 4.0 | % | ASTM D638 |
| Flexural Strength | |||
| 23℃ | 240 | MPa | ASTM D790 |
| Flexural Modulus | |||
| 23℃ | 11000 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0-6.0 | Hr | |
| Rear Temperature Zone 1 | 315-330 | ℃ | |
| Middle Temperature Zone 2 | 320-335 | ℃ | |
| Front Temperature Zone 3 | 325-340 | ℃ | |
| Die temperature | 325-340 | ℃ | |
| Mold Temperature | 90-140 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |