| LOTRYL® 20MA08 is a random copolymer of Ethylene and Methyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the methyl acrylate content, LOTRYL® 20MA08 can be used for applications where softness, flexibility and polarity are required. Typical applications are extrusion coating, coextrusion and compounds.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EMA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Random copolymer,Soft |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.0 to 9.0 | g/10min | ISO 1133 |
| 190℃，2.16kg | 7.0 to 9.0 | g/10min | ASTM D1238 |
| Methacrylic acid content | 18.0 to 22.0 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw A, molded | 83 | ASTM D2240 | |
| Shaw A, molded | 83 | ISO 868 | |
| tensile strength | |||
| Fracture, molded | 9.00 | MPa | ISO 527-2 |
| Fracture, molded | 9.00 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 800 | % | ASTM D638 |
| Fracture, molded | 800 | % | ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 20.0 | MPa | ISO 178 |
| Compression Molding | 20.0 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 46.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | 46.0 | ℃ | ISO 306/A |
| Melting temperature | 76.0 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 150 to 170 | °C | |
| Barrel 2 zone temperature | 170 | °C | |
| Barrel 3 zone temperature | 170 | °C | |
| Barrel 4 zone temperature | 170 | °C | |
| Nozzle temperature | 170 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |