| HFDA-5630 Black is a medium thermal carbon black-filled vulcanizable polyethylene copolymer wire insulation material. It is recommended for use in 600-volt power cable and control cable applications. Specifications HFDA-5630 Black is listed by Underwriters Laboratories for use in XHHW, XHHW-2, RHH, RHW, RHW-2, SIS, USE and USE-2 applications. Cables insulated with HFDA-5630 Black, using sound commercial fabrication practice, should meet the following industry cable specifications: ICEA: S-66-524; NEMA WC7&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | PE copolymerization |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 17.9 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 430 | % | ASTM D412 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength retention rate | |||
| 14 days，150℃ | 100 | % | ASTM D412 |
| Elongation retention rate | |||
| 14 days，150℃ | 87 | % | ASTM D412 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -80.0 | ℃ | ASTM D746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| 3.18 mm | 15 | kV/mm | ASTM D149 |
| 3.18 mm | 14 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 5.00 | ASTM D150 | |
| Dissipation factor | |||
| 60 Hz | 6.0E-3 | ASTM D150 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 48 | ASTM D2240 | |
| Tensile modulus | |||
| Secant | 80.7 | MPa | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel temperature | 66 | °C | |
| Melt temperature | 116 to 135 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F20 |
| 3. Method A (Short-Time) |
| 4. Method B (Step-by-Step) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |