| About |
|---|
| Lucalen G3710E is a maleic anhydride grafted polyethylene resin with a high thermal stability and good flexibility. Lucalen G3710E is primarily designed to be used as the adhesive layer between the top coat polyethylene and the epoxy layer in a 3-layer coating system with easy processing charcteristics. Lucalen G3710E is available in pellet form.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good heat aging resistance,Good flexibility,Good bond,Copolymer,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.931 | g/cm³ | ISO 1183 |
| Apparent density | > 0.50 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.5 | g/10min | ISO 1133 |
| water content | < 0.10 | % | ISO 15512 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| peel strength | DIN 30670 | ||
| 23℃ | > 20.0 | kN/m | DIN 30670 |
| 80℃ | > 4.0 | kN/m | DIN 30670 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -56.7 | ℃ | ASTM D746 |
| Vicat Softening Temp | |||
| A50 | > 100 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 125 | ℃ | ISO 3146 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 51 | ISO 868 | |
| Tensile modulus | |||
| 23℃ | 400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 12.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 700 | % | ISO 527-2/50 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 215 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |