CYCOLAC™ S157 Resin

About
CYCOLAC™ Resin S157是一种高流动性,UL94 V0阻燃，具有良好加工性能的ABS，适用于需要减小厚度的应用

Product Description
Supplier	SABIC
Generic	ABS
Material Status	Commercial: Active
Availabilitys	Africa & Middle East ,North America,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Taber wear and tear
CS-17, 1 kg	145	mg/1000cy	Internal Method
tensile strength
Fracture, 50 mm/min	35	MPa	ISO 527
Fracture, 5 mm/min	35	MPa	ISO 527
Yield, 50 mm/min	45	MPa	ISO 527
Yield, 5 mm/min	40	MPa	ISO 527
Tensile strain
Fracture, 5 mm/min	10	%	ISO 527
Fracture, 50 mm/min	10	%	ISO 527
Yield, 5 mm/min	2	%	ISO 527
Yield, 50 mm/min	2	%	ISO 527
Tensile modulus
1 mm/min	2700	MPa	ISO 527
bending strength	70	MPa	ISO 178
Bending modulus	2500	MPa	ISO 178
Ball hardness
Roche R	112		ISO 2039-2
H358/30	100	MPa	ISO 2039-1

IMPACT	Nominal value	Unit	Test method
Notched impact strength of cantilever beam
-30℃，80104	55	kJ/m²	ISO 180/1U
23℃，80104	NB	kJ/m²	ISO 180/1U
Impact strength of cantilever beam notch
-30℃，80104	4	kJ/m²	ISO 180-1A
23℃，80104	9	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
23 ℃, 80 * 10 * 4, 62mm span	8	kJ/m²	ISO 179/1eA
-23 ℃, 80 * 10 * 4, 62mm span	3	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Thermal conductivity coefficient
23-60℃	0.2	W/m/℃	ISO 8302
Linear coefficient of thermal expansion
TD：23~60℃	8.E-05	1/℃	ISO 11359-2
MD：23~60℃	8.E-05	1/℃	ISO 11359-2
Ball pressure test
75℃±2℃	PASSES		IEC 60695-10-2
Ball pressure test
Approximately maximum	84	℃	IEC 60695-10-2
Vicat Softening Temp	80	℃	ISO 306
Vicat Softening Temp	86	℃	ISO 306
Hot deformation temperature
1.8 MPa, unannealed, 100 mm span	74	℃	ISO 75/Be
0.45 MPa, unannealed, 100 mm span	81	℃	ISO 75/Be
Relative heat index
Non mechanical impact performance	60	℃	UL 746B
Mechanical impact performance	60	℃	UL 746B

PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate
For stretching rods, MD	0.4-0.7	%	Internal Method
Density	1.18	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	1	%	ISO 62
23℃，50% RH	0.2	%	ISO 62
Melt Volume Rate
220℃，5 kg	16	cm³/10min	ISO 1133
220℃，10 kg	72	cm³/10min	ISO 1133
Melt Flow Rate
220℃，5.0kg	17	g/10min	ISO 1133
220℃，10.0kg	78	g/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	>1.E+15	ohms·cm	IEC 60093
Surface resistivity	>1.0E+15		IEC 60093
Insulation failure strength
In oil, 3.2 mm	18	kV/mm	IEC 60243-1
In oil, 1.6 mm	26	kV/mm	IEC 60243-1
In oil, 0.8 mm	35	kV/mm	IEC 60243-1
Relative permittivity
1 MHz	2.7		IEC 60250
Dissipation factor
50-60 Hz	0.005		IEC 60250
Dissipation factor
1 MHz	0.01		IEC 60250
Compared to the leakage tracing index	450	V	IEC 60112
Relative permittivity
50-60 Hz	2.8		IEC 60250

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.50 mm	V-0		UL 94
2.50 mm	5VA		UL 94
3.00 mm	5VB		UL 94
Glowing wire flammability index
960 ℃, passed through	1	mm	IEC 60695-2-12
Oxygen reading value	28	%	ISO 4589

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	80 – 85	°C
Drying time	2 – 4	hrs
Maximum water content	0.1	%
Melt temperature	180 – 210	°C
Spray nozzle temperature	180 – 210	°C
Front temperature	185 – 205	°C
Mid section temperature	185 – 205	°C
Post stage temperature	170 – 190	°C
Hopper temperature	60 – 80	°C
Mold temperature	40 – 80	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.